產(chǎn)品用途：
用于制作高溫真空爐中的發(fā)熱部件、隔熱部件以及裝料器皿等耐高溫器件；用于制作化工業(yè)中蒸煮器、加熱器、冷卻器等耐腐蝕器皿；在航空航天、醫(yī)療植入以及半導(dǎo)體電子等領(lǐng)域均有廣泛應(yīng)用。
Application:
They are used to make high temperature resistant devices such as heating parts, heat insulation parts and charging vessels in the high-temperature vacuum furnace, as well as corrosion-resistant utensils such as digesters, heaters and coolers in the chemical industry. They are also widely used in the fields of aerospace, medical implant and semiconductor electronics.
產(chǎn)品性能參數(shù)/Product Property Parameters：
|
牌號Grade
|
Ta1
|
TaW2.5
|
TaW10
|
|
主含量
Main Content, (%)
|
Ta
|
99.95, min
|
余量
Balance
|
余量
Balance
|
|
化學(xué)成分Chemical Compositions（%，不大于/max）
|
C
|
0.01
|
0.01
|
0.01
|
|
N
|
0.005
|
0.01
|
0.01
|
|
H
|
0.0015
|
0.0015
|
0.0015
|
|
O
|
0.015
|
0.015
|
0.015
|
|
Nb
|
0.02
|
0.05
|
0.05
|
|
Fe
|
0.005
|
0.01
|
0.01
|
|
Ti
|
0.002
|
0.01
|
0.01
|
|
W
|
0.005
|
2.0-3.5
|
9.0-11.0
|
|
Mo
|
0.005
|
0.02
|
0.02
|
|
Si
|
0.005
|
0.005
|
0.005
|
|
Ni
|
0.002
|
0.01
|
0.01
|
|
機械性能
（退火態(tài)）Mechanical Properties（Annealing）
|
抗拉強度
Tensile Strength
（MPa，不小于/min）
|
207
|
276
|
482
|
|
屈服強度
Yield strength
（MPa，不小于/min）
|
138
|
207
|
379
|
|
伸長率
Elongation
（％，最小/min）
|
20
|
20
|
15
|
尺寸/Dimensions:（mm）
|
|
厚度（毫米）
Thickness(mm)
|
寬度（毫米）
Width(mm)
|
長度（毫米）
Length(mm)
|
|
卷帶
Coil Strip
|
0.05-0.30
|
≤200
|
-
|
|
板片
Sheets&Plates
|
0.1-0.5
|
≤600
|
≤2000
|
|
0.5-3.0
|
≤900
|
≤3000
|
|
3.0-8.0
|
≤600
|
≤2000
|
注：如有特殊要求，雙方具體商定.
Note: Special requirements will be agreed upon by the supplier and buyer.